Effect of Titanium Inoculation on Tribological Properties of High Chromium Cast Iron

Open access

Abstract

The present investigation focuses on the study of the influence of titanium inoculation on tribological properties of High Chromium Cast Iron. Studies of tribological properties of High Chromium Cast Iron, in particularly the wear resistance are important because of the special application of this material. High Chromium Cast Iron is widely used for parts that require high wear resistance for example the slurry pumps, brick dies, several pieces of mine drilling equipment, rock machining equipment, and similar ones. Presented research described the effects of various amounts of Fe-Ti as an inoculant for wear resistance. The results of wear resistance were collated with microstructural analysis. The melts were conducted in industrial conditions. The inoculation was carried out on the stream of liquid metal. The following amount of inoculants have been used; 0.17% Fe-Ti, 0.33% Fe-Ti and 0.66% Fe-Ti. The tests were performed on the machine type MAN. The assessment of wear resistance was made on the basis of the weight loss. The experimental results indicate that inoculation improve the wear resistance. In every sample after inoculation the wear resistance was at least 20% higher than the reference sample. The best result, thus the smallest wear loss was achieved for inoculation by 0.66% Fe-Ti. There is the correlation between the changing in microstructure and wear resistance. With greater amount of titanium the microstructure is finer. More fine carbides do not crumbling so quickly from the matrix, improving the wear resistance.

[1] Qiang Liu (2012). Control of Wear-Resistant Properties in Ti-added Hypereutectic High Chromium Cast Iron. Department of Materials Science and Engineering Royal Institute of Technology, Stockholm, Sweden.

[2] Baotong Lu, Jingli Luo, Stefano Chiovelli (2006) Corrosion and Wear Resistance of Chrome White Irons-A Correlation to Their Composition and Microstructure. Metallurgical and Materials Transactions A. vol. 37A, 3029-3038.

[3] Chung, R.J., Tanga, X. Li, D.Y., Hinckley, B. & Dolman, K. (2009). Effects of titanium addition on microstructure and wear resistance of hypereutectic high chromium cast iron Fe-25wt.%Cr-4wt.%C. Wear. 267, 356-361.

[4] Studnicki, A., Dojka, R., Gromczyk, M. & Kondracki, M. (2016). Influence of Titanium on Crystallization and Wear Resistance of High Chromium Cast Iron. Archives of Foundry Engineering. 16(1), 117-123.

[5] Kopyciński, D., Guzik, E., Siekaniec, D. & Szczęsny A. (2015). The effect of addition of titanium on the structure and properties of High Chromium Cast Iron Archives of Foundry Engineering. 15(3), 35-38.

[6] Studnicki, A. (2013). Role of selected inoculants in crystallization of wear resistant high chromium cast iron. Monography. Katowice-Gliwice: Archives of Foundry Engineering. (in Polish).

[7] Kopyciński, D., Siekaniec, D., Szczęsny, A. Nowak, A. & Sokolnicki, M. (2016). The Althoff-Radtke test adapted for high chromium cast iron Archives of Foundry Engineering. 16(4), 61-64.

[8] Zumelzu, E., Goyos, I., Cabezas, C., Opitz, O. & Parada, A. (2002). Wear and corrosion behavior of high-chromium (14- 30% Cr) cast iron alloys. Journal of Materials Processing Technology. 128, 250-255.

[9] Wang, Y.P., Li, D.Y., Parent, L. & Tian, H. (2011). Improving the wear resistance of white cast iron using a new concept -High-entropy microstructure. Wear. 271, 1623-1628.

[10] Bedolla-Jacuinde, A., Correa, R., Mej´ıa, I., Quezada, J.G. & Rainforth, W.M. (2007). The effect of titanium on the wear behavior of a 16%Cr white cast iron under pure sliding. Wear. 263, 808-820.

Archives of Foundry Engineering

The Journal of Polish Academy of Sciences

Journal Information


CiteScore 2016: 0.42

SCImago Journal Rank (SJR) 2016: 0.192
Source Normalized Impact per Paper (SNIP) 2016: 0.316

Metrics

All Time Past Year Past 30 Days
Abstract Views 0 0 0
Full Text Views 184 184 11
PDF Downloads 113 113 16